NC273LT Low Temperature
NO CLEAN SOLDER PASTE
![](https://www.aimsolder.com/wp-content/uploads/No-Clean-Sn-Pb-Paste-500g-Jar-300x300.gif)
Eigenschaften
- Designed for low temperature solder applications
- Increased wetting attributes
- Reduce HiP (Head-in-Pillow) defects
- > 8-hour long stencil life
- Minimize solder balling
- Excellent transfer efficiencies
- RoHS compliant
NC273LT Low Temperature Solder Paste
AIM’s NC273LT Low Temperature Solder Paste features a revolutionary activator system that enhances wetting performance, prolongs stencil life, and achieves excellent transfer efficiencies. Additionally, it effectively minimizes solder balling, a common issue with high bismuth materials.
Low temperature solder materials like NC273LT also decrease peak reflow temperature requirements to as low as 170°C to 175°C (340°F to 350°F). This reduction in temperature leads to cost savings, lower CO2 emissions, and reduced HiP defects.
*bleifreie Legierungen
- Reduces BGA warpage, which minimizes HiP and NWO (Non-Wet Open) defects
- Lowers process temperatures for thin or temperature sensitive components
- Used in step soldering or second-solder reflow applications to exploit the different melting temperatures of two alloys
- Reduces carbon footprint and energy costs
- Lowers material and component costs
Legierungen | Schmelztemperaturen (℃) | Peak Reflow Temperature Range (℃) | Eigenschaften der Legierung |
---|---|---|---|
Sn42/Bi58 | 138°C | 163°C-188°C | • High purity • Eutectic alloy • Low melting temperature |
Sn42/Bi57/Ag1 | 138°C- 140°C | 163°C-188°C | • High purity • Low melting temperature • Addition of Ag increases ductility |
*T4 powder mesh size is standard. Additional powder sizes and alloys may be available upon request.
Wenn das von Ihnen benötigte Dokument nicht in der Liste aufgeführt ist, wenden Sie sich bitte an Ihren AIM-Kundendienstvertreter vor Ort oder Kontaktieren Sie uns um das Dokument anzufordern.
- NC273LT Product Line Card
- NC273LT TDS - Englisch